W, La添加Sm2Fe17N3粉末の磁気特性と微細組織

粉体および粉末冶金 2020 年 67 巻 12 号 p. 682-687

2020年12月15日(火)

松浦 昌志,鈴木 志歩,山本 邦子,手束 展規,杉本 諭

Abstract

The magnetic properties and microstructure of the W and/or La added Sm-Fe-N magnetic powders were investigated. The W and La+W added Sm-Fe-N powders exhibited higher coercivity of 2.1 and 2.0 MAm-1 than that of the powder without La and W addition (1.5 MAm-1), while the La added powder had lower coercivity of 1.0 MAm-1. Initial recoil curves of each powders indicated that volume fraction of single domain particles was higher in the W and La+W added powders than in the La added powder, and the coercivity of these powders strongly depended on particles size. Microstructural observation revealed that W tended to condense in the small particle, and the W was detected from Sm2Fe17N3(0-11) plane.


その他特記事項

This work was (in part) supported by the Elements Strategy Initiative Center for Magnetic Materials (ESICMM), Grant Number JPMXP0112101004, through the Ministry of Education, Culture, Sports, Science and Technology (MEXT).


研究活動

文部科学省

文部科学省
元素戦略プロジェクト(活動紹介)
NIMS磁石パートナーシップ

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合