High-coercivity Nd–Fe–B thick films without heavy rare earth additions

Acta Materialia, Volume 61, Issue 13, Pages 4920–4927, 2013

2013年5月31日(金)

N.M.Dempsey、T.G.Woodcock、H.Sepehri-Amin、Y.Zhang、H.Kennedy、D.Givord、K.Hono and O.Gutfleisch

Abstract

The magnetic properties and microstructures of two Nd–Fe–B thick films with different Nd contents have been studied. The films were deposited in the amorphous state and were crystallized by post-deposition annealing. Both films show a strong 〈0 0 1〉 fibre texture out-of-plane. The film with the higher Nd content has a large room temperature coercivity of 2.7 T, while the one with the lower Nd content has a room temperature coercivity of only 0.7 T. The difference in coercivity may be explained by the fact that the film with the higher Nd content exhibits a continuous Nd-rich grain boundary phase, giving better isolation of the Nd2Fe14B grains with respect to magnetic exchange interactions. The extrusion of Nd-rich liquid to the top surface of the film with high Nd content during post-deposition annealing led to the formation of ripples in the Ta capping layer, indicating that the films are under compressive stress. This stress-induced flow of the Nd-rich material up through the film explains the excellent distribution of the Nd-rich grain boundary phase. Atom probe tomography has revealed the presence of Cu in the Nd-rich grain boundary phase, explaining the formation of the liquid phase at the relatively low temperature of 550 °C due to the eutectic reaction of Nd and Cu.




研究活動

文部科学省

文部科学省
元素戦略プロジェクト(活動紹介)
NIMS磁石パートナーシップ

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合