(Pr0.75Ce0.25)-Fe-B hot-deformed magnets for cryogenic applications

Scripta Materialia Volume 194, 15 March 2021, 113648

2020年12月2日(水)

XinTang, Jiawei Lai, H.Sepehri-Amin, T.Ohkubo, K.Hono

Abstract

We explored the possibility of Pr-Fe-B and (Pr0.75Ce0.25)-Fe-B based hot-deformed magnets as magnetic field source for cryogenic magnetic refrigeration. Thanks to the elimination of spin reorientation effect in the rare earth (RE)-Fe-B system, Pr-Fe-B based hot-deformed magnet shows a large remanence of µ0Mr = 1.75 T with a coercivity of 7.4 T at 20 K. To our surprise, (Pr0.75Ce0.25)-Fe-B based hot-deformed magnet shows even higher remanence of 1.76 T with a coercivity of 4.8 T at 20 K. The measured maximum energy product of the anisotropic (Pr0.75Ce0.25)-Fe-B hot-deformed magnets is 612 kJ/m3 at 20 K, demonstrating their potential as a low-cost permanent magnet for cryogenic applications.




研究活動

文部科学省

文部科学省
元素戦略プロジェクト(活動紹介)
NIMS磁石パートナーシップ

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合