アークプラズマ蒸着法による複合磁性ナノ粒子の作製

粉体および粉末冶金

2017年7月1日(土)

松浦 昌志、五十嵐 拓也、山本 鉄郎、手束 展規、杉本 諭 (  https://doi.org/10.2497/jjspm.64.364 )

Abstract

In this study, magnetic nanoparticles were prepared by the arc plasma deposition (APD). Themonodisperse Fe-Pt nanoparticles (5~10 nm) were obtained on the surface of SiO2nanoparticles. Deposition voltage and shot counts can control particle size of Fe-Pt. Thecoercivity of Fe-Pt/SiO2 composite particles increased after annealing at 300 ℃, and themaximum coercivity value reached to 583 kA・m-1. In the selected area diffraction patternobtained by transmission electron microscopy (TEM), amount of the order L10 phase wasincreased by annealing at 300 ℃. The Mn-Bi nanoparticles (5~20 nm) were also prepared byAPD. The Mn-Bi was deposited on Fe nanoparticles, which were prepared by hydrogen-plasma-meta-reaction (HPMR) method, and monodisperse Mn-Bi particles were obtained onthe Fe nanoparticles. Consequently, the arc plasma deposition is effective process to preparecomposite magnetic nanoparticles.



研究活動

文部科学省

文部科学省
元素戦略プロジェクト(活動紹介)
NIMS磁石パートナーシップ

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合