ホーム > 研究活動 > 口頭発表(2018) > The effects of Zr on intrinsic properties of (Sm1-xZrx)(Fe0.8Co0.2)12 compound with ThMn12 structure

研究活動

The effects of Zr on intrinsic properties of (Sm1-xZrx)(Fe0.8Co0.2)12 compound with ThMn12 structure

日本金属学会2018年秋期(第163回)講演大会

2018年9月20日(木)

TOZMAN KARANIKOLAS Plelin、高橋有紀子、SEPEHRI AMIN Hossein、小川大介、廣澤哲、宝野和博

Abstract

Zr is essential to stabilize ThMn12 structure for ingots with reduced Ti content which arepotential permanent magnets. The effects of Zr on intrinsic magnetic properties of (Sm1-xZrx) (Fe0.8Co0.2)12 is investigated and compared with non-doped Sm (Fe0.8Co0.2)12. Theincrease of Zr substitution for Sm from x= 0 to 0.26 for (Sm1-x Zrx) (Fe0.8Co0.2) 12 increasessaturation magnetization (μ0Ms) from 1.78 T to 1.90 T and decreases anisotropy field, μ0Haand Curie temperature, Tc. The largest μ0Ha and Tc for Zr-doped samples is found 9.8 T and671 K for x=0.18 which is superior to those for Nd2Fe14B. Sm-rich, Sm1.30Zr0.27(Fe0.8Co0.2)12 has high μ0Mr=1.52T and (BH) max=304kJ/m3 which is suitable for hard magnetic thinfilm applications.


研究活動

文部科学省

文部科学省
元素戦略プロジェクト(活動紹介)
NIMS磁石パートナーシップ

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合