NdFe12Nx hard-magnetic compound with high magnetization and anisotropy field

Scripta Materialia

2014年9月13日(土)
(2014.09.13 更新)

Scripta Materialia ( vol 95 Jan.2015 P70–72 (doi:10.1016/j.scriptamat.2014.10.016) )
Y. Hirayama, Y.K. Takahashi, S.Hirosawa,K.Hono

Abstract

The NdFe12Nx compound with a ThMn12 structure (space group I4/mmm) was successfully synthesized by nitriding an NdFe12 layer grown on a W underlayer on a single-crystallineMgO(001) substrate. The c-axis expanded from 0.480 to 0.492 nm while the a-axis showed a slightcontraction from 0.852 to 0.849 nm after the nitriding. Excellent intrinsic hard magnetic propertiesof μ0Ms ≈ 1.66 ± 0.08 T, μ0Ha ≈ 8 T, and Tc ≈ 550 °C, which are superior to those ofNd2Fe14B, were obtained.

その他特記事項

This work was in part supported by JST, CREST.


研究活動

元素戦略拠点

触媒・電池元素戦略拠点
触媒・電池元素戦略研究拠点 (京都大学)
東工大元素戦略拠点
東工大元素戦略拠点 (東京工業大学)
構造材料元素戦略研究拠点
構造材料元素戦略研究拠点 (京都大学)
高効率モーター用磁性材料技術研究組合
高効率モーター用 磁性材料技術研究組合